Faapitoa AtaPolyester fua faatatau atae masani ona faʻaaogaina mo taʻavale taʻavale ma tusiata tioata ata. O se ata sili ona lelei ma le polyester o le vaega autu, ma le sili atu moli moli ma UV tetee. O lona fausaga e masani ona aofia ai le tele o vaega o Polyester ata tifaga, faʻamautinoaina le malosi o le tino malosi ma le tumau. O lenei ata e le gata o lona mama, Ae e lelei foʻi le faʻaleleia o le malutaga ma le saogalemu o le saogalemu, ma mafai ona fetuunai i tulaga eseese o tau o tau.
O le ata faʻataʻitaʻi o le masani ai o le sitaili 8-vaega o le faʻamalama ata o loʻo faʻaalia i lalo.
Fagafao base atafausaga ata
La matou faamalama ataPolyester base atatele aofia ai tolu faʻataʻitaʻiga: sfw11 ma masani uiga, sfw21 ma le maualuga faʻamatalaga ma sfw31 i luga o le ultra-maualuga faamatalaina.
I totonu o latou, o vaega autu o le SFW11 faʻataʻitaʻiga o: maualalo luga o le mamafa, lelei mafolafola, manuia le malosi ma lelei uiga lelei.
Pepa pepa
O le mafiafia o le SFW11 e aofia ai: 25μm, 36μm ma le 50μm etc.
| Meatotino | Iunite | Masani Tau | Suʻega metotia | |||
| Mafiafia | μm | 23 | 36 | 50 | ASTM D374 | |
| Malosi le malosi | MD | Mpa | 181 | 203 | 180 | ASTTM D882 |
| TD | Mpa | 251 | 258 | 250 | ||
| Faasolosolo | MD | % | 159 | 176 | 152 | |
| TD | % | 102 | 113 | 120 | ||
| Suavai malulu | MD | % | 1.12 | 1.11 | 1.02 | ASTM D1204(150℃× 30min) |
| TD | % | 0.27 | 0.11 | 0.14 | ||
| Le Comiction of Fercation | μs | - | 0.37 | 0.47 | 0.39 | ASTM D1894 |
| μd | - | 0.28 | 0.35 | 0.33 | ||
| Lafotu | % | 90.7 | 90.6 | 90.5 | ASTM D1003 | |
| Nifo | % | 1~2 fetuunai | ||||
| Susu susu | Dyne / cm | 52 | 52 | 52 | ASTTM D2578 | |
| Foliga mai | - | OK | Emtco metotia | |||
| Faamatalaga | Luga o lemasani lavaTulaga taua, a le mautinoa taua. Afai o tagata faʻatau e iai manaʻoga faapitoa, e tusa ai ma le konekarate faʻapitoa pulega. | |||||
O le Dream Trust Trust Suʻega e mafai ona faʻaaogaina i le Corona Disc ata.
I le faʻaopopoga i 'oloa na faʻailoa mai i lenei tusitusigawww.dongfonfag-inlation.com.